In the present study, we have revealed that (NiCoFeCr)100-xPdx (x= 1, 3, 5, 20 atom%) high-entropy alloys (HEAs) have both local- and long-range lattice distortions by utilizing X-ray total scattering, X-ray diffraction, and extended X-ray absorption fine structure methods. The local lattice distortion determined by the lattice constant difference between the local and average structures was found to be proportional to the Pd content. A small amount of Pd-doping (1 atom%) yields long-range lattice distortion, which is demonstrated by a larger (200) lattice plane spacing than the expected value from an average structure, however, the degree of long-range lattice distortion is not sensitive to the Pd concentration. The structural stability of these distorted HEAs under high-pressure was also examined. The experimental results indicate that doping with a small amount of Pd significantly enhances the stability of the fcc phase by increasing the fcc-to-hcp transformation pressure from ~13.0 GPa in NiCoFeCr to 20-26 GPa in the Pd-doped HEAs and NiCoFeCrPd maintains its fcc lattice up to 74 GPa, the maximum pressure that the current experiments have reached.
Keywords: lattice distortion; phase transformation; solid-solution alloys.