The steam oxidation behavior of three heterogeneous HR3C alloys was investigated at 650 °C comparatively. After a long-term oxidation process for 1000 h, the results demonstrated that the commercial HR3C alloy already exhibited a high oxidation resistance. However, the spallation resistance of the oxide scale was low during the initial oxidation period. The addition of a moderate amount of Nb into the alloy (1#HR3C) increased the oxidation resistance of the alloy. In addition, the improvement of the microstructural stability was substantially influenced by solid solution strengthening and fine grain strengthening. However, the addition of excessive Nb could significantly affect the growth model of the oxide scale and negatively affect the oxidation performance and microstructural evolution of the alloy (2#HR3C).
Keywords: austenitic stainless steel; microstructural evolution; oxidation behavior; steam oxidation.