A raw montmorillonite (Mt) was submitted to different acidic activation times in order to investigate the influence of the strength and the nature (Brønsted and Lewis) of acidic sites on the synergistic action with an intumescent formulation (IF) composed of ammonium polyphosphate (APP) and pentaerythritol (PER) when incorporated into a polypropylene (PP) matrix. The acidity of the Mt samples was quantified by ammonia temperature-programmed desorption (TPD-NH3) and Fourier transform infrared spectroscopy (FTIR) with pyridine adsorption. The mineral clays were also characterized by X-ray fluorescence (XRF), X-ray diffraction (XRD), nitrogen adsorption analysis and particle size distribution. Thermogravimetric analysis (TGA), limit oxygen index (LOI) and UL-94 were performed to evaluate the flame-retardant properties and the thermal stability. The TGA results show that the final residue increased 2 to 3 fold in comparison to the values predicted theoretically. The flammability properties achieved a maximum for the system containing an excess of moderate-strength Brønsted sites relative to the Lewis ones, reaching 38% in the LOI test. This result suggests that the presence of these Brønsted acidic sites is important, as they take part in the esterification reaction between APP and PER which gives rise to the char formation. The FTIR-Pyr adsorption and flammability results indicate that both the nature and strength of the acidic sites influence the flame-retardant properties.
Keywords: acidic montmorillonite; flame retardancy; intumescence; polypropylene; pyridine adsorption; synergistic agents.