A solvent-vapor transport route produces centimeter-sized single-crystal red phosphors. The epitaxial growth route to yield its core-shell structure at ambient temperature was adopted. These red phosphors could be applied in all-inorganic WLED devices. Cs2 TiF6 :Mn4+ (CTFM) single crystal provides enhancement of quantum efficiency, moisture resistance, and thermal stability compared to polycrystalline powders. The internal quantum efficiency can reach as high as 98.7 %. To further improve waterproof stability, the Cs2 TiF6 (CTF) shell with tunable thickness has been epitaxially grown on the CTFM single crystal surface and a unique three-step photoluminescence intensity evolution mechanism has been proposed. By combining as-prepared CTFM@CTF core-shell structured single crystal, YAG:Ce single crystal and blue-chip, warm WLEDs with excellent color rendition (Ra =90, R9 =94), low correlated color temperature (CCT=3155 K), and high luminous efficacy were fabricated without any organic resins.
Keywords: core-shell structures; light-emitting diodes; manganese; single crystals; water resistance.
© 2020 Wiley-VCH GmbH.