In the last decade, particulate matter (PM) has gradually become a serious public health issue due to its harmful impact on the human body. In this study, we report a novel filtration system for high PM capturing, based on the magnetoelectric (ME) effect that induces an effective surface charge in membrane filters. To elucidate the ME effect on PM capturing, we prepared electrospun poly(vinylidene fluoride)(PVDF)/CoFe2O4(CFO) membranes and investigated their PM capturing efficiency. After electrical poling under a high electric field of 10 kV/mm, PM-capturing efficiencies of the poled-PVDF/CFO membrane filters were improved with carbon/fluorine(C/F) molar ratios of C/F = 4.81 under Hdc = 0 and C/F = 7.01 under Hdc = 700 Oe, respectively. The result illustrates that electrical poling and a dc magnetic field could, respectively, enhance the surface charge of the membrane filters through (i) a strong beta-phase alignment in PVDF (poling effect) and (ii) an efficient shape change of PVDF/CFO membranes (magnetostriction effect). The diffusion rate of a water droplet on the PVDF/CFO membrane surface is reduced from 0.23 to 0.05 cm2/s by covering the membrane surface with PM. Consequently, the PM capturing efficiency is dramatically improved up to 175% from ME membranes with the poling process and applying a magnetic field. Furthermore, the PM was successfully captured on the prototype real mask derived from the magnetoelectric effect induced by a permanent magnet with a diameter of 2 cm without any external power.
Keywords: capturing efficiency; cobalt ferrite oxide; magnetoelectric membrane filters; particulate matter; poly(vinylidene fluoride).