Biodentine is a calcium silicate cement (CSC) that has been broadly applied in vital pulp therapy. The quality of the Biodentine-composite bond has a significant effect on the longevity of the definitive restoration. The aim of this study is to investigate the shear bond strength (SBS) between Biodentine and composite restoration at different maturation times of Biodentine aged in artificial saliva. Fifteen Biodentine discs were allocated into three groups (n = 5) based on the timeframe of performance of composite restoration: immediate (after 12 min), after 14 days, and after 28 days of Biodentine maturation. Total etch and rinse adhesive system and bulk-fill regular resin composite were used. The shear bond strength and the failure pattern were assessed. One-way ANOVA with the Bonferroni post hoc test was applied for statistical analysis at p < 0.05. The highest (32.47 ± 8.18 MPa) and the lowest (4.08 ± 0.81 MPa) SBS values were recorded for 14 days and 12 min groups, respectively. Significant statistical differences were reported among the groups, and a high statistically significant difference was found between the immediate group and the other groups. Adhesive failure patterns were evident in all groups. More clinically acceptable bond strength between the Biodentine and overlaid composite restoration is at 14 days after Biodentine maturation. Delaying the coverage of Biodentine later than 14 days may significantly reduce the SBS. Using the artificial saliva as an aging medium may affect the SBS between Biodentine and composite material.
Copyright © 2020 Ruba M. Mustafa et al.