This paper studies the mechanical properties of porous asphalt concrete with styrene-butadiene-styrene (SBS) polymer modified bitumen as the binder, steel slag as the aggregate and crumb rubber and basalt fiber as modifiers. First, the appearance, mechanics, chemical composition and high-temperature stability of steel slag were studied by some equipment. Then, three kinds of porous asphalt concrete with SBS polymer modified bitumen as binder were produced, Namely, crumb rubber modified porous asphalt concrete (CR-PAC), basalt fiber modified porous asphalt concrete (BF-PAC), and basalt fiber and crumb rubber composite modified asphalt concrete (CM-PAC). Finally, the properties of the three kinds of modified PACs were studied through the Marshall test, freeze-thaw splitting test, low-temperature splitting test, permeability test, and creep test. The results showed that the crush value and abrasion value of steel slag are 15.1% and 13.5%, respectively; it has excellent strength and abrasion. In addition, the steel slag shows a porous structure and it provides an interface basis for a better bond with bitumen. For the three PACs, the results showed that the Marshall stability, water stability, and low-temperature crack resistance of CM-PAC are all the best Furthermore, CM-PAC has better rutting resistance than two single modified PACs, based on creep test results. The CM-PAC in this study can be used as a new type of pavement material.
Keywords: SEM analysis; XRF spectroscopy; pavement performance; porous asphalt concrete; steel slag; styrene-butadiene-styrene.