Tantalum (Ta) and its application in biomaterials has been attracting more and more attention recently. It can be considered as a material for hard tissue implants. This study focuses on antimicrobial and surface characterization of micro-arc oxidized (MAO) nanocrystalline Ta compared with its microcrystalline equivalent. For the purposes of the investigation, x-ray diffractometry (XRD), scanning electron microscopy (SEM), atomic force microscopy (AFM), wetting analysis, optical profilometry, corrosion resistance measurement, and antimicrobial tests were performed. Nanocrystalline Ta was fabricated using high-energy ball milling (HEBM) and pulse plasma sintering (PPS). The MAO process done at 250 V results in the formation of a porous oxide surface. An XRD analysis confirmed the presence of a Ta2 O5 oxide layer. Based on the SEM pictures, the obtained oxide layer was approximately 3-4 μm thick for nanocrystalline Ta substrate. For microcrystalline Ta, the oxide layer was thinner, in the range of 0.3-0.6 μm. The analysis of polarization curves showed a significant improvement of corrosion resistance for MAO nanocrystalline Ta (2.62 × 10-8 A/cm2 ) versus not oxidized nanocrystalline Ta (1.20 × 10-5 A/cm2 ). The surface roughness of MAO nanocrystalline Ta proved to be several times higher than that of unoxidized Ta. Wetting analysis showed that the oxide layer on the nanocrystalline substrate is hydrophilic. This research provides detailed information about MAO microcrystalline and MAO nanocrystalline Ta antimicrobial activity against Staphylococcus aureus and Pseudomonas aeruginosa. A significant decrease of S. aureus for MAO nanocrystalline Ta (control 10,435 ± 981 vs. sample 3,453 ± 130) was noticed. No significant difference was noticed for MAO microcrystalline and nanocrystalline Ta tested for P. aeruginosa.
Keywords: antimicrobial activity; micro-arc oxidation; nanocrystalline tantalum; surface characterization.
© 2020 Wiley Periodicals LLC.