High-Temperature Hydrogen Sensing Performance of Ni-Doped TiO2 Prepared by Co-Precipitation Method

Roussin Lontio Fomekong; Klemens Kelm; Bilge Saruhan

doi:10.3390/s20215992

High-Temperature Hydrogen Sensing Performance of Ni-Doped TiO₂ Prepared by Co-Precipitation Method

Sensors (Basel). 2020 Oct 22;20(21):5992. doi: 10.3390/s20215992.

Authors

Roussin Lontio Fomekong^{1

2}, Klemens Kelm², Bilge Saruhan²

Affiliations

¹ Higher Teacher Training College, University of Yaounde I, Yaounde P.O. BOX 47, Cameroon.
² German Aerospace Center (DLR), Institute of Materials Research, 51147 Cologne, Germany.

Abstract

This work deals with the substantially high-temperature hydrogen sensors required by combustion and processing technologies. It reports the synthesis of undoped and Ni-doped TiO₂ (with 0, 0.5, 1 and 2 mol.% of Ni) nanoparticles by a co-precipitation method and the obtained characteristics applicable for this purpose. The effect of nickel doping on the morphological variation, as well as on the phase transition from anatase to rutile, of TiO₂ was investigated by scanning electron microscopy, X-ray diffraction and Raman spectroscopy. The resistive sensors prepared with these powders were tested toward H₂ at 600 °C. The results indicate that 0.5% Ni-doped TiO₂ with almost equal amounts of anatase and rutile shows the best H₂ sensor response (ΔR/R0 = 72%), response rate and selectivity. The significant improvement of the sensing performance of 0.5% Ni-doped TiO₂ is mainly attributed to the formation of the highest number of n-n junctions present between anatase and rutile, which influence the quantity of adsorbed oxygen (i.e., the active reaction site) on the surface and the conductivity of the material.

Keywords: Ni-doped TiO2; co-precipitation; gas sensor; high-temperature sensing; hydrogen.