The molecular processes that accompany dynamic mechanical response to large deformations at high strain rate (≈1000 s-1 or higher) underlie the early stages of damage in materials, but understanding of material response in this regime is typically limited to macroscopic constitutive equations. Here, spiropyran mechanophores are embedded in very short, stress-bearing strands in silicone elastomers, and their mechanochromic response to uniaxial compression is explored in a Split Hopkinson Pressure (or Kolsky) Bar. At strain rates of 1000 s-1 , the onset of mechanochromism occurs at lower strains, but higher stresses, than in the same materials under quasi-static loading. Similar to quasi-static loading, however, a negligible effect of mechanophore structure on the critical strain for colorimetric onset is observed. The results suggest that nonequilibrium, inhomogeneous local tension distributions in the elastomers lead to greater stress in individual strands than at the same strains under equilibrium loading, but that within the regions of force concentration, mechanochromic onset is determined primarily by a limiting local strain threshold.
Keywords: Kolsky bar; high rate loading; mechanochemistry; spiropyran.
© 2020 Wiley-VCH GmbH.