Impurity element doping is extensively taken as one of the most efficient strategies to regulate the electronic structure as well as the rate of photogenerated charge separation of photocatalysts. Herein, a one-pot hydrothermal synthesis process was exploited to obtain La-doped ZnIn2S4 microspheres, aiming at gaining insight into the role that doping ions played in the improvement of pollutant photodegradation. Systematical characterization means, comprising of X-ray photoelectron spectroscopy (XPS), ultraviolet-visible (UV-vis) diffuse reflection spectroscopy and Raman spectra, combination with high-resolution transmission electron microscopy (HRTEM), were employed to in depth reveal the concomitancy of La ions and ZnIn2S4 crystal lattice. The results showed that the La-doped ZnIn2S4 samples exhibited a slightly wider and stronger spectral absorption than pristine ZnIn2S4; and the specific surface area of doped ZnIn2S4 samples was a bit larger. The La-doped ZnIn2S4 electrodes showed improved photocurrent response, and the photocurrent density reached a maximum value at La content of 1.5 wt%. As expected, La-doped ZnIn2S4 samples exhibited a remarkable enhancement of photocatalytic behaviour toward the photodegradation of tetracycline hydrochloride (TCH) and methyl orange (MO). The prominently enhanced photoactivity of doped ZnIn2S4 samples was due to the synergistic effect of the elevated visible-light absorption ability and effective photogenerated charge carriers' separation.
Keywords: ZnIn2S4; doping; photocatalytic degradation; visible-light.