Three different metal oxides (basic MgO, basic-acidic Al2O3 and acidic-basic Nb2O5) characterized by comparable surface areas (MgO-130 m2/g; Al2O3-172 m2/g and Nb2O5-123 m2/g) and pore systems (domination of mesopores with narrow pore size distribution) were modified with tris(2-aminoethyl)amine (TAEA) via two methods: (i) direct anchoring of amine on metal oxide and (ii) anchoring of amine on metal oxide functionalized with (3-chloropropyl)trimethoxysilane. The obtained hybrid materials were characterized in terms of effectiveness of modifier anchoring (elemental analysis), their structural/textural properties (nitrogen adsorption/desorption, XRD), acidity/basicity of support (2-propanol dehydration and dehydrogenation, dehydration and cyclization of 2,5-hexanedione), states of modifier deposited on supports (XPS, FTIR, UV-VIS) and the strength of interaction between the modifier and the support (TG/DTG). It was evidenced that acidic-basic properties of metal oxides as well as the procedure of modification with TAEA determined the ways of amine anchoring and the strength of its interaction with the support. The obtained hybrid materials were tested in Knoevenagel condensation between furfural and malononitrile. The catalysts based on MgO showed superior activity in this reaction. It was correlated with the way of TAEA anchoring on basic MgO and the strength of modifier anchoring on the support. To the best of our knowledge tris(2-aminoethyl)amine has not been used as a modifier of solid supports for enhancement of the catalyst activity in Knoevenagel condensation.
Keywords: Knoevenagel condensation; TAEA; acidity; basicity; mesoporous oxides.