This paper uses polypropylene (PP) as the matrix and acrylic acid (AA) and maleic anhydride (MAH) as functional monomers to prepare PP-g-(AA-MAH) fibers by suspension grafting and melt-blown spinning technology that are easy to industrially scale-up. The fibers can be used to adsorb aniline. Results showed that the grafting ratio reached the maximum of 12.47%. The corresponding optimal conditions were grafting time of 3 h, AA: MAH = 0.75, total monomer content of 55%, benzoyl peroxide 1.4%, xylene concentration of 6 mL/g PP, and deionized water content of 8 mL/g PP. Owing to its good fluidity and thermal stability, the product of suspension grafting can be used for melt-blown spinning. Infrared spectroscopic and nuclear magnetic resonance spectroscopic analyses indicated that AA and MAH were successfully grafted onto PP fibers. After grafting, the hydrophilicity of PP-g-(AA-MAH) fiber increased. Therefore, it had higher absorptivity for aniline and the adsorption capacity could reach 42.2 mg/g at 45 min and pH = 7. Moreover, the PP-g-(AA-MAH) fibers showed good regeneration performance.
Keywords: adsorption; aniline; melt-blown spinning; polypropylene; suspension grafting.