The effect of TiO2 nanoparticles on the photophysical properties of ternary conjugated polymer (CP) blends of poly(9,9-dioctylfluorene-2,7-diyl) (PFO), poly 9,9-dioctylfluorene-alt-benzothiadiazole (F8BT) and poly(2-methoxy-5(2-ethylhexyl)-1,4 -phenylenevinylene (MEH-PPV) thin films was investigated. This ternary blend used a fixed amount of PFO as the donor with MEH-PPV and F8BT in various ratios as the acceptors. The solution-blending method and the spin-coating technique were used to prepare the blends and the thin films, respectively. Through efficient Förster Resonance Energy Transfer (FRET), the desired white emission was achieved with PFO/0.3 wt.% F8BT/0.5 wt.% MEH-PPV ternary blend thin film. Additions of nanoparticles up to 10 wt.% dramatically intensified the white emission which then dimmed at higher contents due to agglomerations. The current density-voltage characteristics of the nanocomposite thin films exhibited dependency on the content and distributions of the nanoparticles. Finally, a possible underlying mechanism for the intensification of emission is proposed.
Keywords: Förster Resonance Energy Transfer; charge trapping effect; exciplex inhibition; nanocomposites.