Multifunctional-imprinted nanocomposite membranes with thermo-responsive biocompatibility for selective/controllable recognition and separation application

Abstract

Inspired by the biomimetic modification strategy of dopamine self-polymerization technique, molecularly imprinted nanocomposite membranes (MINCMs) with thermo-responsive rebinding and separation performance were synthesized and evaluated. Herein, the Au/SiO₂-based multilevel structure had been successfully obtained onto the polydopamine (pDA) modified membrane surfaces. Afterward, the poly(N-isopropylacrylamide)-based biomolecule-imprinted sites were adequately constructed by developing a photoinitiated atom transfer radical polymerization (pATRP) imprinting strategy using the high-biocompatible ovalbumin (Ova, pI 4.6) as template molecule. Therefore, thermo-responsive 'specific recognition sites' toward Ova were then achieved on the as-prepared MINCMs after the well-designed imprinting process. When the external temperature was set at 37 °C, excellent ovalbumin rebinding capacity (33.26 mg/g), selectivity factor (3.06) and structural stability were obtained. Importantly, as to the controllable biocompatibility research of this work, the bare glass and Ova-bound-MINCMs (the MINCMs were bound with Ova) showed basically the same cell adhesion behaviors and viability, indicating the excellent biocompatibility of the Ova-bound-MINCMs. Additionally, efficient and rapid regulation of cell adhesion/detachment on ovalbumin-bound MINCMs could be still obtained even after 10 cycles of temperature-switch process, which indicated that the as-prepared MINCMs had strong ability to work under high intensity and long continuous operation.

Keywords: Au/SiO(2)-polydopamine nanocomposite; Bioinspired biomolecule-imprinted methodology; Controllable cell adhesion/detachment; Selective recognition and separation; Thermo-responsive membranes.