High-voltage direct-current (HVDC) dry bushing capacitor-core insulation is composed of epoxy resin-impregnated insulating paper (RIP). To improve the thermal conductivity, breakdown strength, and space charge characteristics of RIP, 0.1 wt % nano-cellulose fiber (CNF)-modified RIP (CNF/RIP), 2.5-30 wt % hexagonal boron nitride (h-BN)-modified RIP (h-BN/RIP), and 2.5-30 wt % h-BN + 0.1 wt % CNF-modified RIP (h-BN + 0.1 wt % CNF/RIP) were prepared. Scanning electron microscopy (SEM) was implemented; the thermal conductivity, DC conductivity, DC breakdown strength, and space charge characteristics were tested. The maximum thermal conductivity of h-BN + 0.1 wt % CNF/RIP was 0.376 W/m.K with a h-BN content of 30 wt %. The thermal conductivity was 85.2% higher than that of unmodified RIP. The breakdown strength and charge suppression were the best in the case of 10 wt % h-BN + 0.1 wt % CNF/RIP. The maximum breakdown strength was 11.2% higher than that of unmodified RIP. These results can play a significant role in the research and development of insulation materials for HVDC dry bushing.
Keywords: dielectric characteristics; dry bushing; epoxy resin-impregnated paper; nanocomposite; space charge; thermal conductivity.