A growing environmental concern is increasing the search for new sustainable materials. In this scenario, natural lignocellulosic fibers (NLFs) became an important alternative to replace synthetic fibers commonly used as composites reinforcement. In this regard, unknown NLFs such as the caranan fiber (Mauritiella armata) found in South American rain forests revealed promising properties for engineering applications. Thus, for the first time, the present work conducted a technical characterization of caranan fiber-incorporated composites. Epoxy matrix composites with 10, 20 and 30 vol% of continuous and aligned caranan fibers were investigated by tensile tests, thermogravimetric analysis (TGA) and differential scanning calorimetry (DSC). Composites with more than 10% vol of caranan fibers significantly increase the elastic modulus and toughness in comparison to the neat epoxy. Indeed, the composite with 30 vol% was 50% stiffer, 130% tougher, and 100% stronger, which characterized an effective reinforcement. As for the elastic modulus, total strain and tensile toughness, there is a clear tendency of improvement with the amount of caranan fiber. The TGA disclosed the highest onset temperature of degradation (298 °C) with the least mass loss (36.8%) for the 30 vol% caranan fiber composite. It also displayed a higher degradation peak at 334 °C among the studied composites. The lowest glass transition temperature of 63 °C was obtained by DSC, while the highest of 113 °C by dynamic mechanical analysis (DMA) for the 30 vol% caranan composite. These basic technical findings emphasize the caranan fiber potential as reinforcement for polymer composites.
Keywords: caranan fibers; natural fiber composite; tensile properties; thermal analysis.