As a natural polymer, gelatin is increasingly being used as a substitute for animals or humans for the simulation and testing of surgical procedures. In the current study, the similarity verification was neglected and a 10 wt.% or 20 wt.% gelatin sample was used directly. To compare the mechanical similarities between gelatin and biological tissues, different concentrations of gelatin samples were subjected to tensile, compression, and indentation tests and compared with porcine liver tissue. The loading rate in the three tests fully considered the surgical application conditions; notably, a loading speed up to 12 mm/s was applied in the indentation testing, the tensile test was performed at a speed of 1 mm/s until fracture, and the compression tests were compressed at a rate of 0.16 mm/s and 1 mm/s. A comparison of the results shows that the mechanical behaviors of low-concentration gelatin samples involved in the study are similar to the mechanical behavior of porcine liver tissue. The results of the gelatin material were mathematically expressed by the Mooney-Rivlin model and the Prony series. The results show that the material properties of gelatin can mimic the range of mechanical characteristics of porcine liver, and gelatin can be used as a matrix to further improve the similarity between substitute materials and biological tissues.
Copyright © 2020 Jiyun Zhao et al.