Graphene-polyamide-6 (PA6) composites with up to 17.0%·w/w graphene content were prepared via melt mixing. Oscillatory rheometry revealed that the dynamic viscoelastic properties of PA6 decreased with the addition of 0.1%·w/w graphene but increased when the graphene content was increased to 6.0%·w/w and higher. Further analysis indicated that the rheological percolation threshold was between 6.0 and 10.0%·w/w graphene. The Carreau-Yasuda model was used to describe the complex viscosity of the materials. Capillary rheometry was applied to assess the steady shear rheology of neat PA6 and the 17.0%·w/w graphene-PA6 composite. High material viscosity at low shear rates coupled with intense shear-thinning in the composite highlighted the importance of selecting the appropriate rheological characterisation methods, shear rates and rheological models when assessing the 3D printability of percolated graphene-polymer composites for material extrusion (ME). A method to predict the printability of an ME filament feedstock, based on fundamental equations describing material flow through the printer nozzle, in the form of a printing envelope, was developed and verified experimentally. It was found that designing filaments with steady shear viscosities of approximately 15% of the maximum printable viscosity for the desired printing conditions will be advantageous for easy ME processing.
Keywords: 3D printing; graphene; material extrusion; printing envelope; rheological properties.