An in vitro assessment of the physical properties of manually- mixed and encapsulated glass-ionomer cements

Lamis Al-Taee; Sanjukta Deb; Avijit Banerjee

doi:10.1038/s41405-020-0040-x

An in vitro assessment of the physical properties of manually- mixed and encapsulated glass-ionomer cements

BDJ Open. 2020 Aug 11:6:12. doi: 10.1038/s41405-020-0040-x. eCollection 2020.

Authors

Lamis Al-Taee¹, Sanjukta Deb², Avijit Banerjee^{2

3}

Affiliations

¹ Department of Conservative and Aesthetic Dentistry, Baghdad College of Dentistry, University of Baghdad, Baghdad, Iraq.
² Oral, Clinical & Translational Sciences, Faculty of Dentistry, Oral & Craniofacial Sciences, King's College London, Guy's Dental Hospital, London, UK.
³ Conservative & MI Dentistry, Faculty of Dentistry, Oral & Craniofacial Sciences, King's College London, King's College London, Guy's Dental Hospital, London, UK.

Abstract

Objectives: The last decade has seen a variety of modifications of glass-ionomer cements (GICs), such as inclusion of bioactive glass particles and dispensing systems. Hence, the aim was to systematically evaluate effect of mixing modes and presence of reactive glass additives on the physical properties of several GICs.

Materials and methods: The physical properties of eight commercial restorative GICs; Fuji IX GP Extra (C&H), Ketac^TM Fill Plus Applicap (C&H), Fuji II LC (C&H), Glass Carbomer Cement and Equia® Forte Fil, capsulated versus manually mixed were assessed. 256 cylindrical specimens were prepared for compressive strength and microhardness, whilst 128 disc-shaped specimens were prepared for biaxial flexural strength tests. Fluid uptake and fluoride release were assessed. Data were analysed using one-way ANOVA and Games-Howell post-hoc tests (alpha = 0.05).

Results: Both encapsulated GIC/RMGICs exhibited significantly improved mechanical properties in comparison to manually mixed equivalents, which in turn showed higher fluid uptake and early fluoride release (p < 0.05). The glass carbomer cement exhibited improved mechanical properties post ageing and evidence of mineral deposits were apparent in the microstructure.

Conclusions: The mixing mode and inclusion of reactive glass additives in cements had a statistically significant effect on physical properties of the selected GICs-RMGICs.