To overcome problems associated with loosening of orthopedic implants and surgical site infections, we developed a novel, titanium (Ti)-based material that releases both strontium and silver ions (CaSrAg-Ti) based on alkali-and-heat treatment. The results of commercially pure Ti (cp-Ti), Ti that releases Sr ions only (CaSr-Ti), and the novel CaSrAg-Ti material were compared. Mechanical tests were performed to evaluate the in vivo bonding properties of CaSrAg-Ti and the bone-implant contact (BIC) ratio in histological specimens was determined at 4 and 8 weeks after implantation in a rat femur. Also, the in vitro antibacterial activities of this material against methicillin-susceptible Staphylococcus aureus (MSSA) were evaluated after a 24 h incubation period by assaying colony-forming units. In addition, antibacterial activities were evaluated in vivo at 7 days after implantation in a rat subcutaneous pocket model. There was direct contact between the bone and CaSrAg-Ti in histological specimens and no apparent signs of argyrosis in any rat. The bone-bonding strength and the BIC ratio were increased by 2.7- and 2.3-fold for CaSrAg-Ti vs. cp-Ti at 4 weeks and 2.2- and 2.0-fold at 8 weeks, respectively. As compared with cp-Ti, the number of viable MSSA remaining on CaSrAg-Ti was reduced by 100 ± 0% in vitro and 94.2 ± 6.9% in vivo. Ti that releases Sr and Ag ions is a promising material that exhibits both bone-bonding properties and anti-MSSA activities.
Keywords: alkali-and-heat treatment; antibacterial activity; silver; strontium; titanium.
© 2020 Wiley Periodicals LLC.