Molybdenum dioxide (MoO2) a kind of semi-metal material shows many unique properties, such as high melting point, good thermal stability, large surface area-to-volume ratio, high-density surface unsaturated atoms, and excellent conductivity. There is a strong connection between structural type and optoelectronic properties of 2D nanosheet. Herein, the rectangular and hexagonal types of thin and thick MoO2 2D nanosheets were successfully prepared from MoO3 powder using two-zone chemical vapor deposition (CVD) with changing the experimental parameters, and these fabricated nanosheets displayed different colors under bright-field microscope, possess margins and smooth surface. The thickness of the blue hexagonal and rectangular MoO2 nanosheets are ~ 25 nm and ~ 30 nm, respectively, while typical thickness of orange-colored nanosheet is around ~ 100 nm. Comparative analysis and investigations were carried out, and mix-crystal phases were indentified in thick MoO2 as main matrix through Raman spectroscopy. For the first time, the emission bands obtained in thick MoO2 nanosheets via a Cathodoluminescence (CL) system exhibiting special properties of semi-metallic and semi-conductors; however, no CL emission detected in case of thin nanosheets. The electrical properties of thin MoO2 nanosheets with different morphologies were compared, and both of them demonstrated varying metallic properties. The resistance of thin rectangular nanosheet was ~ 25 Ω at ± 0.05 V while 64 Ω at ± 0.05 V was reported for hexagonal nanosheet, and observed lesser resistance by rectangular nanosheet than hexagonal nanosheet.
Keywords: Chemical vapor deposition (CVD); Hexagonal; Molybdenum dioxide nanosheets; Rectangular.