Driven by the rapid development of additive manufacturing technologies and the trend towards mass customization, the development of new feedstock materials has become a key aspect. Additivation of the feedstock with nanoparticles is a possible route for tailoring the feedstock material to the printing process and to modify the properties of the printed parts. This study demonstrates the colloidal additivation of PA12 powder with laser-synthesized carbon nanoparticles at >95% yield, focusing on the dispersion of the nanoparticles on the polymer microparticle surface at nanoparticle loadings below 0.05 vol%. In addition to the descriptors "wt%" and "vol%", the descriptor "surf%" is discussed for characterizing the quantity and quality of nanoparticle loading based on scanning electron microscopy. The functionalized powders are further characterized by confocal dark field scattering, differential scanning calorimetry, powder rheology measurements (avalanche angle and Hausner ratio), and regarding their processability in laser powder bed fusion (PBF-LB). We find that heterogeneous nucleation is induced even at a nanoparticle loading of just 0.005 vol%. Finally, analysis of the effect of low nanoparticle loadings on the final parts' microstructure by polarization microscopy shows a nanoparticle loading-dependent change of the dimensions of the lamellar microstructures within the printed part.
Keywords: 3D printing; Nanocomposites; additive manufacturing; colloidal additivation; laser fragmentation in liquids; polyamide; selective laser sintering SLS.