A novel composite of poly(3-aminobenzoic acid) (PABA) and a cobalt zeolitic benzimidazolate framework (CoZIF) has been studied for the production of hydrogen through the hydrogen evolution reaction (HER). The structural characteristics and successful synthesis of PABA, CoZIF and the PABA/CoZIF composite were confirmed and investigated using different techniques. Probing-ray diffraction for phase analysis revealed that the composite showed a decrease and shift in peak intensities, confirming the incorporation of CoZIF on the PABA backbone via in situ polymerization, with an improvement in the crystalline phase of the polymer. The thermal stability of PABA was enhanced upon composite formation. Both scanning electron microscopy and transmission electron microscopy showed that the composite had a rough surface, owing to an interaction between the CoZIF and the external surface of the PABA. The electrochemical hydrogen evolution reaction (HER) performance of the synthesized samples was evaluated using cyclic voltammetry and Tafel analysis. The composite possessed a Tafel slope value of 156 mV/dec and an α of 0.38, suggesting that the Volmer reaction coupled with either the Heyrovsky or Tafel reaction as the rate determining step. The fabricated composite showed high thermal stability and excellent tolerance as well as high electroactivity towards the HER, showing it to be a promising non-noble electrocatalyst to replace Pt-based catalysts for hydrogen generation.
Keywords: Tafel analysis; electrocatalyst; hydrogen evolution reaction; metal organic frameworks; poly(3-aminobenzoic acid).