The effects of build orientation and heat treatment on the crack growth behavior of 316L stainless steel (SS) fabricated via a selective laser melting additive manufacturing process were investigated. Available research results on additively manufactured metallic parts still require a substantial expansion. The most important issue connected with the metal properties after additive manufacturing are the high anisotropy properties, especially from the fatigue point of view. The study examined the crack growth behavior of additively manufactured 316L in comparison to a conventionally made reference material. Both groups of samples were obtained using precipitation heat treatment. Different build orientations in the additively manufactured samples and rolling direction in the reference samples were taken into account as well. Precipitation heat treatment of additively manufactured parts allowed one to achieve microstructure and tensile properties to similar to those of conventionally made pieces. The heat treatment positively affected the fatigue properties. Additionally, precipitation heat treatment of additively manufactured elements significantly affected the reduction of fatigue cracking velocity and changed the fatigue cracking mechanism.
Keywords: 316L steel; additive manufacturing; fatigue cracking; selective laser melting.