We describe the impact of tensile strains on the structural properties of thin films composed of PffBT4T-2OD π-conjugated polymer and PC71BM fullerenes coated on a stretchable substrate, based on a novel approach using in situ studies of flexible organic thin films. In situ grazing incidence X-ray diffraction (GIXD) measurements were carried out to probe the ordering of polymers and to measure the strain of the polymer chains under uniaxial tensile tests. A maximum 10% tensile stretching was applied (i.e., beyond the relaxation threshold). Interestingly we found different behaviors upon stretching the polymer: fullerene blends with the modified polymer; fullerene blends with the 1,8-Diiodooctane (DIO) additive. Overall, the strain in the system was almost twice as low in the presence of additive. The inclusion of additive was found to help in stabilizing the system and, in particular, the π-π packing of the donor polymer chains.
Keywords: additive; conjugated polymer and blends; in situ GIXD; strain; structure.