Cesium lead halide perovskite nanocrystals (PNCs), while possessing facile chemical synthesis routes and high photoluminescence (PL) properties, are still challenged by issues of instability and degradation. Although atomic layer deposition (ALD) of metal oxides has been one of the common encapsulation approaches for longer term stability, its application inevitably resulted in severe loss of emission efficiency and at times partial loss of structural integrity of perovskites, creating a bottleneck in its practical viability. We demonstrate a nondestructive modified gas-phase technique with codeposition of both precursors trimethylaluminum and water to dramatically enhance the PL emission in zero-dimensional (0D) Cs4PbBr6 PNCs via alumina encapsulation. X-ray photoelectron spectroscopy analysis of Cs4PbBr6 films reveals the alumina deposition to be accompanied by elemental composition changes, particularly by the reduction of the excessive cesium content. Ab initio density functional theory simulations further unfold that the presence of excess Cs on the surface of PNCs leads to decomposition of structural [PbBr6]4- octahedra in the 0D perovskite lattice, which can be prevented in the presence of added hydroxyl groups. Our study thus unveils the pivotal role of the PNC surface composition and treatment in the process of its interaction with metal oxide precursors to control the PL properties as well as the stability of PNCs, providing an unprecedented way to use the conventional ALD technique for their successful integration into optoelectronic and photonic devices with improved properties.
Keywords: alumina encapsulation; atomic layer deposition; defect states; perovskite nanocrystals; photoluminescence; photonic devices; stability; surface passivation.