Objective: The present study aimed to evaluate the bending resistance and cyclic fatigue fracture resistance of a new single-file reciprocating instrument called WaveOne Gold. Reciproc and WaveOne instruments were used as references for comparison.
Methods: Sixty 25-mm NiTi instruments (Reciproc R25, WaveOne Primary and WaveOne Gold Primary) were tested. Flexibility was determined by applying 45° bending tests using a universal testing machine (n=10). A custom-made device was used during cyclic fatigue test (n=10), comprising a stainless steel artificial canal measuring 1.4 mm in diameter, 19 mm in total length with an 86° angle and 6 mm radius of curvature. Possible deformations at the helical shaft and mode of fracture were evaluated using scanning electron microscopy analysis. Statistical analysis was performed using one-way analysis of variance. Post hoc pair-wise comparisons were performed using Tukey's test for multiple comparisons (P<0.05).
Results: WaveOne presented significantly higher bending resistance than the other tested systems (P<0.05), whereas Reciproc presented the lowest bending resistance (P<0.05). Reciproc revealed a significantly longer cyclic fatigue fracture resistance than the other systems (P<0.05).
Conclusion: Although WaveOne Gold presented higher flexibility than WaveOne, no differences in the resistance to fatigue were observed between both systems. The Reciproc files were more flexible and resistant to fatigue for the angle of curvature of 86° and 6 mm radius than WaveOne and WaveOne Gold files.
Keywords: Bending resistance; NiTi alloy; WaveOne Gold; cyclic fatigue; reciprocating movement.