This study was aimed at the production and characterization of coated cotton textiles with luminescent ceramic nanophases doped with cationic Ir(III) tetrazole complexes. We confirmed that SiO2 nanoparticles (NPs) do not affect the phosphorescent properties of the complexes that maintain their emission (610 and 490 nm). For the first time we transferred the luminescence feature from nanosol to textile surface, highlighting the advantages of using nanosilica as an encapsulating and stabilizing matrix. The optimized Ir@SiO2 suspensions were homogenously applied onto the cotton surface by dip-pad-dry-cure technique, as proved by the 2p-fluorescence microscope analysis. Once we verified the self-marker properties of the Ir(III) complex, we observed an excellent washing fastness of the coating with a very limited release. SiO2 in the washing water was quantified at maximum around 1.5 wt% and Ir below the inductively coupled plasma optical emission spectrometry (ICP-OES) detection limit of 1 ppm. A Franz cell test was used to evaluate any possible ex-vivo uptake of Ir@SiO2 nanoparticles across human skin tissues, showing that epidermis and dermis stop over 99% of Ir, implying a reduced impact on human health. The light-induced antimicrobial potential of the Ir@SiO2 were assessed toward both Gram(-) and Gram(+) bacteria. The results encouraged further developments of such functional textiles coated by self-markers and antibacterial active nanophases.
Keywords: antibacterial properties; cotton textiles; iridium (III) luminescent complexes; silica host matrix; singlet oxygen.