In this study, a set of advanced characterization techniques were used to evaluate the morphological, structural, and thermal properties of a novel molecular hybrid based on silica nanoparticles/hydrolyzed polyacrylamide (CSNH-PC1), which was efficiently obtained using a two-step synthetic pathway. The morphology of the nanohybrid CSNH-PC1 was determined using scanning electron microscopy (SEM), dynamic light scattering (DLS), and nanotracking analysis (NTA) techniques. The presence of C, N, O, and Si atoms in the nanohybrid structure was verified using electron dispersive scanning (EDS). Moreover, the corresponding structural analysis was complemented using powder X-ray diffraction (XRD) and attenuated total reflection-Fourier transform infrared spectroscopy (ATR-FT-IR). The covalent bond between APTES-functionalized SiO2 nanoparticles (nSiO2-APTES), and the hydrolyzed polyacrylamide (HPAM) chain (MW ≈ 20.106 Da) was confirmed with high-resolution X-ray spectroscopy (XPS). Finally, the thermal properties of the nanohybrid were evaluated by using thermogravimetric analysis (TGA) and differential scanning calorimetry (DSC). The results showed that the CSNH-PC1 has a spherical morphology, with sizes between 420-480 nm and higher thermal resistance compared to HPAM polymers without modification, with a glass transition temperature of 360 °C. The integration of these advanced characterization techniques implemented here shows promising results for the study and evaluation of new nanomaterials with multiple applications.
Keywords: characterization of polymers; nanohybrids; nanomaterials; nanoparticles; synthetic polymers.