Graphene-encapsulated iron nanoparticles (Fe(G)) hold great promise as microwave absorbers owing to the combined dielectric loss of the graphene shell and the magnetic loss of the ferromagnetic metal core. Transmission electron microscopy (TEM) revealed transition metal nanoparticles encapsulated by graphene layers. The microwave electromagnetic parameters and reflection loss (R) of the Fe(G) were investigated. Graphene provided Fe(G) with a distinctive dielectric behavior via interfacial polarizations taking place at the interface between the iron cores and the graphene shells. The R of Fe(G)/paraffin composites with different Fe(G) contents and coating thickness was simulated according to the transmit-line theory and the measured complex permittivity and permeability. The Fe(G)/paraffin composites showed an excellent microwave absorption with a minimum calculated R of -58 dB at 11 GHz and a 60 wt% Fe(G) loading. The composites showed a wide bandwidth (the bandwidth of less than -10 dB was about 11 GHz). The R of composites with 1-3 mm coating thickness was measured using the Arch method. The absorption position was in line with the calculated results, suggesting that the graphene-coated iron nanoparticles can generate a suitable electromagnetic match and provide an intense microwave absorption. Excellent Fe(G) microwave absorbers can be obtained by selecting optimum layer numbers and Fe(G) loadings in the composites.
Keywords: graphene-encapsulated iron nanoparticles; microwave absorption; permittivity and permeability; reflection loss; simulation.