The characteristic changes in steelmaking slag and humic acids (HAs) derived from a slag-compost fertilizer and their relation to the elution of Fe were evaluated in tank tests in Mashike, Hokkaido and Tsushima, Nagasaki. Analyses of iron, nitrogen and phosphate in the eluate, changes in the chemical states on the surface of the steelmaking slag, and the macro-structural features of the isolated HAs were investigated during the test. Temporal changes in Fe concentrations in the tanks were consistent with data collected in previous studies. Analyses of the surface by 57Fe Mössbauer spectroscopy showed that the concentration of Fe2+ in the fertilizer decreased and the ratio of Fe3+ increased, indicating that Fe2+ was preferentially eluted from the slag surface. The yields of HAs were significantly decreased during the test when steelmaking slag was mixed with compost. Changes in the UV-vis absorptivities indicated that de-aromatization had occurred. These results indicate that microorganisms that were present under these experimental conditions became activated by the mixing of compost with steelmaking slag, and are closely related to the continuous elution of Fe. The residual Fe in the fertilizer after the tests was investigated by analyzing seawater and the levels of extractable Fe. The trends for extractable Fe concentrations were consistent with the results obtained by 57Fe Mössbauer spectroscopy and UV-vis spectra.
Keywords: 57Fe Mössbauer spectroscopy; Iron elution; UV-vis parameter; compost; humic acids; seawater; steelmaking slag.