Enhanced NiO Dispersion on a High Surface Area Pillared Heterostructure Covered by Niobium Leads to Optimal Behaviour in the Oxidative Dehydrogenation of Ethane

Abstract

A Nb-containing siliceous porous clay heterostructure (PCH) with Nb contents from 0 to 30 wt %) was prepared from a bentonite and used as support in the preparation of supported NiO catalysts with NiO loading from 15 to 80 wt %. Supports and NiO-containing catalysts were characterised by several physicochemical techniques and tested in the oxidative dehydrogenation (ODH) of ethane. The characterisation studies on Nb-containing supports showed the presence of well-anchored Nb⁵⁺ species without the formation of Nb₂ O₅ crystals. High dispersion of nickel oxide with low crystallinity was observed for the Nb-containing PCH supports. In addition, when NiO is supported on these Nb-containing porous clays, it is more effective in the ODH of ethane (ethylene selectivity of ca. 90 %) than NiO supported on the corresponding Nb-free siliceous PCH or on Nb₂ O₅ (ethylene selectivities of ca. 30 and 60 %, respectively). Factors such as the NiO-Nb⁵⁺ interaction, the NiO particle size and the properties of surface Niⁿ⁺ species were shown to determine the catalytic performance.

Keywords: dehydrogenation; nickel; niobium; porous heterostructures; supported catalysts.