Synthesis of Palladium-Based Crystalline@Amorphous Core-Shell Nanoplates for Highly Efficient Ethanol Oxidation

Abstract

Phase engineering of nanomaterials (PEN) offers a promising route to rationally tune the physicochemical properties of nanomaterials and further enhance their performance in various applications. However, it remains a great challenge to construct well-defined crystalline@amorphous core-shell heterostructured nanomaterials with the same chemical components. Herein, the synthesis of binary (Pd-P) crystalline@amorphous heterostructured nanoplates using Cu_{3- χ} P nanoplates as templates, via cation exchange, is reported. The obtained nanoplate possesses a crystalline core and an amorphous shell with the same elemental components, referred to as c-Pd-P@a-Pd-P. Moreover, the obtained c-Pd-P@a-Pd-P nanoplates can serve as templates to be further alloyed with Ni, forming ternary (Pd-Ni-P) crystalline@amorphous heterostructured nanoplates, referred to as c-Pd-Ni-P@a-Pd-Ni-P. The atomic content of Ni in the c-Pd-Ni-P@a-Pd-Ni-P nanoplates can be tuned in the range from 9.47 to 38.61 at%. When used as a catalyst, the c-Pd-Ni-P@a-Pd-Ni-P nanoplates with 9.47 at% Ni exhibit excellent electrocatalytic activity toward ethanol oxidation, showing a high mass current density up to 3.05 A mg_Pd ^-1 , which is 4.5 times that of the commercial Pd/C catalyst (0.68 A mg_Pd ^-1 ).

Keywords: amorphous; ethanol oxidation reaction; heterostructures; nanoplates.