Here, a thin and foldable porous reduced graphene oxide (rGO) fabricated by a solvent casting method (SC-rGO) is introduced. The SC-rGO is superior to aluminum as a positive triboelectric material in triboelectric nanogenerators (TENGs), significantly enhancing TENG output performance. The film shows extremely foldable features, where it could be folded by 1/16 size. The electrical properties and device performance of SC-rGO are optimized varying thicknesses from 5 to 30 µm. A 30 µm thick TENG with a non-annealed SC-rGO film (STENG) shows the highest output of about 255 µW cm-2 due to its high carrier concentration, low work function, and high surface area. After annealing, STENG performance is optimized with a 10 µm thick SC-rGO because their work functions decreases, while the corresponding carrier concentrations decrease according to the thickness of the SC-rGO films. The SC-rGO films are highly durable and stable, where their output and conductivity show negligible changes after 100 000 cycles of mechanical deformation. A large SC-rGO with a size of 13 × 3 cm2 is fabricated and is attached inside a person's arm to demonstrate the shape-adaptive characteristics. Consequently, 170 V is obtained and it turns on 19 green light emitting diodes by simply touching the STENG.
Keywords: light emitting diodes; reduced graphene oxide; solvent casting; triboelectric materials; triboelectric nanogenerators.
© 2020 The Authors. Published by WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.