The rapid screening of plutonium from aqueous sources remains a critical challenge for nuclear nonproliferation efforts. The determination of trace-level Pu isotopes in water requires offsite sample preparation and analysis; therefore, new methods that combine plutonium purification, concentration, and isotopic screening in a fieldable detection system will provide an invaluable tool for nuclear safeguards. This contribution describes the development and characterization of thin polymer-ligand films for the isolation and concentration of waterborne Pu for direct spectroscopic analyses. Submicron thin films were prepared through spin coating onto Si wafers and consisted of combinations of polystyrene (PS) with dibenzoylmethane, thenoyltrifluoroacetone, and di(2-ethylhexyl)phosphoric acid (HDEHP). Pu uptake studies from solutions at pH from 2.3 to 6.3 indicated that only films containing HDEHP exhibited significant recovery of Pu. High alpha spectroscopy peak energy resolutions were achieved for PS-HDEHP films over a range of film thicknesses from 30 to 250 nm. A separate study was performed to evaluate uptake from a primarily Pu(V) solution where it was observed that doubling the HDEHP loading in the film increased uptake of Pu by an order of magnitude. X-ray photoelectron spectroscopy (XPS) analysis revealed that HDEHP was highly concentrated within the first few nanometers of the film at the higher loading. XPS analysis also revealed that, in the presence of water, HDEHP was stripped from the surface layer of the film at circumneutral pH. While significant losses of ligand were seen in all samples, higher loadings of HDEHP resulted in measurable amounts of ligand retained after a 12-h soak in water. Findings of this study are being used to guide the development of thin-film composite membrane-based detection methods for the rapid, fieldable analysis of Pu in water.