In this work, functionalized multi-walled carbon nanotubes (MWCNT) were synthesized by the reaction between acylated MWCNT and 10-(2,5-dihydroxyphenyl)-9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide (ODOPB). The obtained MWCNT-ODOPB was well dispersed into epoxy resins together with aluminum diethylphosphinate (AlPi) to form flame-retardant nanocomposites. The epoxy resin nanocomposite with phosphorus content of 1.00 wt % met UL 94 V-0 rating, exhibited LOI value of 39.5, and had a higher Tg compared to neat epoxy resin, which indicates its excellent flame retardant performance. These experimental results indicated that MWCNT-ODOPB was a compatible and efficient flame retardant for epoxy resins. Moreover, cone calorimeter analysis showed that the peak heat release rate (pHRR), total heat release (THR) values, and CO2 production profiles of the composites decreased with an increase in the additional amount of phosphorus.
Keywords: DOPO; epoxy resin; flame retardant; functionalized MWCNTs; nanocomposites.