Electrochemical and thermodynamic study on the corrosion performance of API X120 steel in 3.5% NaCl solution

Khuram Shahzad; Mostafa H Sliem; R A Shakoor; A Bahgat Radwan; Ramazan Kahraman; Malik Adeel Umer; Umair Manzoor; Aboubakr M Abdullah

doi:10.1038/s41598-020-61139-3

Electrochemical and thermodynamic study on the corrosion performance of API X120 steel in 3.5% NaCl solution

Sci Rep. 2020 Mar 9;10(1):4314. doi: 10.1038/s41598-020-61139-3.

Authors

Khuram Shahzad^#¹, Mostafa H Sliem^#², R A Shakoor³, A Bahgat Radwan², Ramazan Kahraman⁴, Malik Adeel Umer⁵, Umair Manzoor¹, Aboubakr M Abdullah⁶

Affiliations

¹ Department of Materials Engineering, School of Chemical and Materials Engineering, National University of Science and Technology (NUST), Islamabad, Pakistan.
² Center for Advanced Materials (CAM), Qatar University, 2713, Doha, Qatar.
³ Center for Advanced Materials (CAM), Qatar University, 2713, Doha, Qatar. shakoor@qu.edu.qa.
⁴ Department of Chemical Engineering, College of Engineering, Qatar University, 2713, Doha, Qatar.
⁵ Department of Materials Engineering, School of Chemical and Materials Engineering, National University of Science and Technology (NUST), Islamabad, Pakistan. umer.adeel@scme.nust.edu.pk.
⁶ Center for Advanced Materials (CAM), Qatar University, 2713, Doha, Qatar. abubakr_2@yahoo.com.

^# Contributed equally.

Abstract

The present work studied the effect of temperature on the corrosion behavior of API X120 steel in a saline solution saturated with CO₂ in absence and presence of polyethyleneimine (PEI) as an environmentally safe green inhibitor. The effect of PEI on the corrosion behavior of API X120 steel was investigated using destructive and non-destructive electrochemical techniques. The overall results revealed that PEI significantly decreases the corrosion rate of API X120 steel with inhibition efficiency of 94% at a concentration of 100 μmol L^-1. The adsorption isotherm, activation energy and the thermodynamic parameters were deduced from the electrochemical results. It is revealed that the adsorption of PEI on API X120 steel surface follows Langmuir adsorption isotherm adopting a Physi-chemisorption mechanism. Finally, the samples were characterized using scanning electron microscopy (SEM) and atomic force microscopy (AFM) techniques to elucidate the effect of aggressiveness of corrosive media on the surface morphology and the corrosion performance of API X120 steel. The surface topography result indicates that the API X120 steel interface in PEI presence is smoother than CO₂ with Cl^- ions or Cl^- ions only. This is attributed to the compact protective film limits the aggressive ions transfer towards the metallic surface and reduces the corrosion rate. Moreover, PEI inhibition mechanism is based on its CO₂ capturing ability and the PEI adsorption on the steel surface beside the siderite layer which give the PEI molecules the ability to reduce the scale formation and increase the corrosion protection due to capturing the CO₂ from the brine solution.