[Research on sintering process of tricalcium phosphate bone tissue engineering scaffold based on three-dimensional printing]

Abstract

Tricalcium phosphate (TCP) is one of the most widely used bioceramics for constructing bone tissue engineering scaffold. The three-dimensional (3D) printed TCP scaffold has precise and controllable pore structure, while with the limitation of insufficient mechanical properties. In this study, we investigated the effect of sintering temperature on the mechanical properties of 3D-printed TCP scaffolds in detail, due to the important role of the sintering process on the mechanical properties of bioceramic scaffolds. The morphology, mass and volume shrinkage, porosity, mechanical properties and degradation property of the scaffold was studied. The results showed that the scaffold sintered at 1 150℃ had the maximum volume shrinkage, the minimum porosity and optimal mechanical strength, with the compressive strength of (6.52 ± 0.84) MPa and the compressive modulus of (100.08 ± 18.6) MPa, which could meet the requirements of human cancellous bone. In addition, the 1 150℃ sintered scaffold degraded most slowly in the acidic environment compared to the scaffolds sintered at the other temperatures, demonstrating its optimal mechanical stability over long-term implantation. The scaffold can support bone mesenchymal stem cells (BMSCs) adherence and rapid proliferation and has good biocompatibility. In summary, this paper optimizes the sintering process of 3D printed TCP scaffold and improves its mechanical properties, which lays a foundation for its application as a load-bearing bone.

Keywords: bone tissue engineering scaffold; mechanical property; sintering technology; three-dimensional printing; tricalcium phosphate.