: Microstructure and corrosion behavior of the solution-treated Mg-1.8Zn-1.74Gd-0.5Y-0.4Zr (wt%) alloy were studied. The results of microstructure indicated that the second phases of as-cast alloy was mainly comprised of Mg12Zn(Gd,Y) phase, Mg3Zn3(Gd,Y)2 phase and (Mg,Zn)3(Gd,Y) phase. After solution treatment process, the second phase gradually dissolved into the matrix, and the grain size increased. The effect of microgalvanic corrosion between α-Mg matrix and second phase was also improved. At the range of 470~510 °C solution treatment temperature, the corrosion resistance of the samples increases at first and then decreases slightly at 510 °C. All the solution-treated Mg-Zn-Gd-Y-Zr samples exhibit better corrosion resistance in comparison with as-cast sample. The existence form of the remaining phase affects the morphology of the corroded surface that relatively complete dissolution with homogeneous microstructure makes the sample more effective to obtain uniform corrosion form. The optimum temperature for solution treatment is 490 °C, which shows a much better corrosion resistance and uniform corrosion form after soaking for a long time.
Keywords: Mg-Zn-Zr-Gd-Y; corrosion; microstructure; solution treatment.