The direct assembly of functional nanoparticles into a highly crystalline mesoporous semiconductor with oriented configurations is challenging but of significance. Herein, an evaporation induced oriented co-assembly strategy is reported to incorporate SnO2 nanocrystals (NCs) into a 3D branched mesoporous TiO2 framework by using poly(ethylene oxide)-block-polystyrene (PEO-b-PS) as the template, SnO2 NCs as the direct tin source, and titanium butoxide (TBOT) as the titania precursor. Owing to the combined properties of ultrasmall particle size (3-5 nm), excellent dispersibility and presence of abundant hydroxyl groups, SnO2 NCs can easily interact with PEO block of the template through hydrogen bonding and co-assemble with hydrolyzed TBOT to form a novel hierarchical branched mesoporous structure (SHMT). After calcination, the obtained composites exhibit a unique 3D flower-like structure, which consists of numerous mesoporous rutile TiO2 branches with uniform cylindrical mesopores (≈9 nm). More importantly, the SnO2 NCs are homogeneously distributed in the mesoporous TiO2 matrix, forming numerous n-n heterojunctions. Due to the unique textual structures, the SHMT-based gas sensors show excellent gas sensing performance with fast response/recovery dynamics, high sensitivity, and selectivity toward ethanol.
Keywords: co‐assembly; gas sensing; heterojunctions; hierarchical structures; mesoporous TiO 2.
© 2019 The Authors. Published by WILEY‐VCH Verlag GmbH & Co. KGaA, Weinheim.