The aim of this study is the analyze the structure of branched polyurethanes based on synthetic poly([R,S]-3-hydroxybutyrate) and their blends with biopolymers and montmorillonite. The properties which would predict the potential susceptibility of these materials to degradation are also estimated. Fourier-transform infrared spectroscopy with attenuated total reflection analysis shows that poly([d,l]-lactide) is on the surfaces of polyurethanes, whereas chitosan and starch are included inside the blend network. Atomic force microscopy images have shown that the surfaces of investigated samples are heterogenous with the formation of spherulites in case of pure polyurethanes. The presence of biopolymers in the blend reduced the crystallinity of polyurethanes. Thermal stability of blends of polyurethanes with poly([d,l]-lactide) and polysaccharides decreased in comparison to pure polyurethanes. Although the tensile strength is reduced after the blending of polyurethanes with biopolymers, the elongation at break increased, especially in the case of polyurethane/poly([d,l]-lactide) blends. The presence of polysaccharides in the obtained blends caused the significant reduction of contact angle after one minute from water drop immersion. This hydrophilizing effect is the highest when montmorillonite has been incorporated into the chitosan blend. The estimated properties of the obtained materials suggest their potential sensitivity on environmental conditions.
Keywords: biopolymers; branched polyurethanes; chemical structure; contact angle; surface morphology; synthetic polyhydroxybutyrate; thermal and mechanical properties.