Fire and smoke suppressions of polyvinyl alcohol (PVA) aerogels are urgently required due to the serious fire hazard they present. MXene, a 2D transition-metal carbide with many excellent properties, is considered a promising synergist for providing excellent flame retardant performance. PVA/ammonium polyphosphate (APP)/transition metal carbide (MXene) composite aerogels were prepared via the freeze-drying method to enhance the flame retardancy. Thermogravimetric analysis, limiting oxygen index, vertical burning, and cone calorimeter tests were executed to investigate the thermal stability and flame retardancy of PVA/APP/MXene (PAM) composite aerogels. The results demonstrated that MXene boosted the flame retardancy of PVA-APP, and that PAM-2 (with 2.0 wt% MXene loading) passed the V-0 rating, and reached a maximum LOI value of 42%; Moreover, MXene endowed the PVA-APP system with excellent fire and smoke suppression performance, as the the peak heat release rate and peak smoke production rate were significantly reduced by 55% and 74% at 1.0 wt% MXene loading. The flame retardant mechanism was systematically studied, MXene facilitated the generation of compact intumescent residues via ita catalyst effects, thus further restraining the release of heat and smoke. This work provides a simple route to improve the flame retardancy of PVA aerogels via the synergistic effect of MXene and APP.
Keywords: MXene; ammonium polyphosphate; polyvinyl alcohol (PVA); synergistic effect.