In order to reduce the influence of CaF2 addition on the mechanical properties of self-lubricating ceramic tools, we applied a silicon dioxide (SiO2) coating on calcium fluoride (CaF2) nanoparticles through hydrolysis and condensation reactions using the tetraethoxysilane (TEOS) method. The powder was dried by the azeotropic method, so that it acquired a better dispersibility. The resulting composite powders were characterized using XRD (X-ray diffraction) and TEM (transmission electron microscopy), showing that the surface of CaF2 was coated with a layer of uniform and compact SiO2. SiO2 shells with different thicknesses could be obtained by changing the amount of TEOS added, and the thickness of the SiO2 shells could be controlled between 1.5 and 15 nm. At the same time, a ceramic material containing CaF2 nanoparticles and CaF2@SiO2-coated nanoparticles was prepared. It had the best mechanical properties when CaF2@SiO2-coated nanoparticles were added; its flexural strength, fracture toughness, and hardness were 562 ± 28 MPa, 5.51 ± 0.26 MPa·m1/2, and 15.26 ± 0.16 GPa, respectively. Compared with the ceramic tool containing CaF2 nanoparticles, these mechanical properties were increased by 17.57%, 12.67%, and 4.88%, respectively. The addition of CaF2@SiO2-coated nanoparticles greatly improved the antifriction and wear resistance of the ceramic material, and the antifriction and wear resistance were balanced.
Keywords: SiO2-coated CaF2; nanoparticles; self-lubricating ceramic tool; solid lubricant.