Triple-Shelled Co-VSe x Hollow Nanocages as Superior Bifunctional Electrode Materials for Efficient Pt-Free Dye-Sensitized Solar Cells and Hydrogen Evolution Reactions

Xing Qian; Weimin Wu; Yudi Niu; Jiahui Yang; Chong Xu; Kwok-Yin Wong

doi:10.1021/acsami.9b16623

Triple-Shelled Co-VSe _x Hollow Nanocages as Superior Bifunctional Electrode Materials for Efficient Pt-Free Dye-Sensitized Solar Cells and Hydrogen Evolution Reactions

ACS Appl Mater Interfaces. 2019 Nov 20;11(46):43278-43286. doi: 10.1021/acsami.9b16623. Epub 2019 Nov 7.

Authors

Xing Qian¹, Weimin Wu¹, Yudi Niu¹, Jiahui Yang¹, Chong Xu¹, Kwok-Yin Wong²

Affiliations

¹ College of Chemical Engineering , Fuzhou University , Xueyuan Road No. 2 , Fuzhou 350116 , China.
² Department of Applied Biology and Chemical Technology and State Key Laboratory of Chemical Biology and Drug Discovery , The Hong Kong Polytechnic University , Hung Hom, Kowloon 999077 , Hong Kong.

PMID: 31663327
DOI: 10.1021/acsami.9b16623

Abstract

Complex nanostructures with distinct spatial architectures and more active sites hold broad prospects in new energy conversion fields. Herein, a facile strategy was carried out to construct triple-shelled Co-VSe_x nanocages, starting with an ion-exchange process between Co-based zeolitic imidazolate framework-67 (ZIF-67) nanopolyhedrons and VO₃^- followed by the formation of triple-shelled Co-VSe_x hollow nanocages during the process of increasing the solvothermal temperature under the assistance of SeO₃^2-. Meanwhile, triple-shelled Co-VS_x and yolk-double shell Co-VO_x nanocages were fabricated as references by a similar process. Benefiting from the larger surface areas and more electrolyte adsorption sites, the triple-shelled Co-VSe_x nanocages exhibited excellent electrocatalytic performances when applied as the electrochemical catalysts for dye-sensitized solar cells (DSSC) and hydrogen evolution reactions (HER). More concretely, the DSSC based on the Co-VSe_x counter electrode showed outstanding power conversion efficiency of 9.68% when its Pt counterpart was 8.46%. Moreover, the Co-VSe_x electrocatalyst exhibited prominent HER performance with a low onset overpotential of 40 mV and a small Tafel slope of 39.1 mV dec^-1 in an acidic solution.

Keywords: Co-VSex; Pt-free catalysts; bifunctional electrocatalysts; dye-sensitized solar cells; hydrogen evolution reactions; triple-shelled nanocages.