In this study, the effect of glass fiber powder on the properties of waterborne coatings with thermochromic ink was investigated, using Chinese fir board as the base material and temperature-sensitive thermochromic waterborne coatings with thermochromic ink as the paint base. The concentration of glass fiber powder was determined when the microstructure, optical properties, mechanical properties, liquid resistance, and heat preservation effect were the best. The results showed that the paint film with glass fiber powder concentration of 1.0% to 7.0% had better discoloration performance. With an increase of the glass fiber powder concentration, the gloss of the paint film decreased gradually, and when the concentration of glass fiber powder was 0% to 5.0%, the gloss of the paint film was better. The concentration of glass fiber powder had no effect on the adhesion, impact resistance, and liquid resistance. In the first 2.5 min, the temperature value of the waterborne coating with 3.0% glass fiber powder was higher than that without glass fiber powder, which has a certain heat preservation effect. When the glass fiber powder content was 3.0%, the microstructure of paint film was the best. The composition of paint film with different glass fiber powder concentrations was not different and the discoloration performance of paint film with heat preservation effect was not affected by time. The analysis showed that the waterborne coating with 3.0% glass fiber powder had the best comprehensive performance. This work provides a technical reference for the industrialization of heat preservation and thermochromic coating on wood.
Keywords: film performance; glass fiber powder; thermochromic ink; waterborne coating.