Low resistivity polycrystalline Si could be selectively grown in the deep (~200 nm) and narrow patterns (~20 nm) of 20 nm pitch design rule DRAM (Dynamic Random Access Memory) by microwave plasma-enhanced chemical vapor deposition (MW-CVD). We were able to achieve the high phosphorus (CVD gap-fill in a large electrical contact area which does is affected by line pitch size) doping concentration (>2.5 × 1021 cm-3) and, thus, a low resistivity by adjusting source gas (SiH4, H2, PH3) decomposition through MW-CVD with a showerhead controlling the decomposition of source gases by using two different gas injection paths. In this study, a selective growth mechanism was applied by using the deposition/etch cyclic process to achieve the bottom-up process in the L-shaped contact, using H2 plasma that simultaneously promoted the deposition and the etch processes. Additionally, the cyclic selective growth technique was set up by controlling the SiH4 flow rate. The bottom-up process resulted in a uniform doping distribution, as well as an excellent filling capacity without seam and center void formation. Thus, low contact resistivity and higher transistor on-current could be achieved at a high and uniform phosphorus (P)-concentration. Compared to the conventional thermal, this method is expected to be a strong candidate for the complicated deep and narrow contact process.
Keywords: gap-fill process; microwave plasma; selective Si growth.