This study assessed the applicability of chitin nanocrystals employed in combination with an existing coating material intended for flexible packaging. The 2,2,6,6-tetramethylpiperidine 1-oxyl (TEMPO) oxidized chitin nanocrystals (TOCNs) were applied 1) as an additive in a water-based acrylic resin (WBAR) that was then coated onto the surface of a biaxially oriented polypropylene (BOPP) film, and 2) as a neat layer in multilayered BOPP laminates bonded by a WBAR adhesive layer. The results indicated that the flow behavior and shear viscosity of the TOCN/WBAR system were dependent on TOCN contents. The TOCNs as a dispersed phase in the acrylic resin matrix did not improve the oxygen barrier property of the resulting coated BOPP. By contrast, the neat continuous TOCN coating layer improved the oxygen barrier property of the laminates of BOPP and TOCNs bonded by the acrylic resin, a 44% oxygen transmission rate reduction for a laminate with a 8.33-μm TOCN layer compared to the laminate without a TOCN layer. The inclusion of the TOCNs maintained the optical transparency of the resulting films.
Keywords: Barrier property; Chitin nanocrystals; Coating; Film; Laminate; Rheology.
Published by Elsevier Ltd.