Enhanced alginate-based microsphere with the pore-forming agent for efficient removal of Cu(Ⅱ)

Abstract

In order to increase the adsorption properties of sodium alginate gel beads, a series of SA@PF-beads (sodium alginate-based beads with different amount of pore-forming agent) were prepared with calcium carbonate as the pore forming agent. The experimental results showed that the adsorption capacity of Cu(Ⅱ) increased by at least two times (from 13.69 mg/g to 33.88 mg/g, treated with SA@PF-0 and SA@PF-2.0, respectively) with proper amount of calcium carbonate added, which is economical and effective. In the experiment, SEM was used to measure the morphology of gel beads with different amount of pore-forming agent. FTIR and XPS were used to analyze the variation of functional groups and bond energies in the adsorption process. Adsorption isotherms and kinetics were conducted and showed that the adsorption process was consistent with Langmuir model and Elovich kinetic model. The maximum Langmuir adsorption 229.746 mg/g. The effects of pH, temperature and solid-liquid ratio on adsorption capacity were also investigated. In brief, calcium carbonate is an efficient and convenient pore-forming agent, which can be used to improve the adsorption properties of alginate gel materials.

Keywords: Adsorption; Cu; Pore-forming agent; Sodium alginate.