Objective: The aim of this study was to evaluate the bone-regeneration efficiency of novel polymeric nanostructured membranes and the effect of zinc, calcium, titanium, and bone morpho-protein loading on membranes, through an in vivo rabbit model.
Material and methods: Nanostructured membranes of methylmethacrylate were loaded with zinc, calcium, TiO2 nanoparticles, and bone-morphogenetic protein (BMP). These membranes covered the bone defects prepared on the skulls of six rabbits. Animals were sacrificed 6 weeks after surgery. Micro computed tomography was used to evaluate bone architecture through BoneJ pluging and ImageJ script. Three histological processing of samples, including von Kossa silver nitrate, toluidine blue, and fluorescence by the deposition of calcein were utilized.
Results: Zn-membranes (Zn-Ms) promoted the highest amount of new bone and higher bone perimeter than both unloaded and Ti-membranes (Ti-Ms). Ca-membranes (Ca-Ms) attained higher osteoid perimeter and bone perimeter than Zn-Ms. The skeleton analysis showed that Zn-Ms produced more branches and junctions at the trabecular bone than BMP-loaded membranes (BMP-Ms). Samples treated with Ti-Ms showed less bone formation and bony bridging processes. Both Zn-Ms and Ca-Ms achieved higher number of osteoblasts than the control group. BMP-Ms and Ca-Ms originated higher number of blood vessels than Ti-Ms and control group.
Conclusions: Zn incorporation in novel nanostructured membranes provided the highest regenerative efficiency for bone healing at the rabbit calvarial defects.
Clinical relevance: Zn-Ms promoted osteogenesis and enhanced biological activity, as mineralized and osteoid new bone with multiple interconnected ossified trabeculae appeared in close contact with the membrane.
Keywords: Bone regeneration; Non-resorbable polymer; Scaffold; Zinc.